Dacrylate High Performance Metal Coatings
Vinadac High Build Sheen Finish

Vinadac High Build Sheen Finish

Reference No.: 41-200

High build vinyl pigmented with durable, light-fast pigments

High build coating for protection of steel and galvanised steel in aggressive environments. Tolerant of damp surfaces during application. Typical applications include lighting columns and general industrial plant.

Colours available: Full range. All BS and RAL colours availabe on Dacmix scheme
Appearance Of Dried Film: Sheen
Volume Solids: 40% (may vary with colour)
Dry Film Thickness: Typical 75 microns
Range 50-120 microns
Theoretical Coverage: 5.3m² per litre at 75 microns
Drying Time At 20°C: Touch Dry: 2 hours
Film Dry: 3 hours
Overcoat: 3 hours
(will vary with temperature, air movements, etc.)
Packaging: 5 litre and 20 litre open-top containers
Shelf Life: 2 years or longer in unopened containers when stored under cover in good storage conditions.
Storage: Under cover with temperature range of 5°C to 32°C.
*Due to the protective nature of the product, some chalking may occur on exposure/weathering. This is purely aesthetic and will not detract from the performance,durability and longevity of the system. It should therefore be borne in mind that this phenomenon may be visible on certain bright/bold colours.
Surface Preparation: Mild steel, clean and free of millscale: Thoroughly degrease using Dacrylate Thinner R5. Apply one coat of Vinaprime 41 HB Anti-Corrosion Primer to a dry film thickness of 50 microns.
Mild steel, corroded and/or millscale present: Abrasive blasting to ISO 8501-1 SA 2.5 is the preferred method.
Manual clean: Chip, scrape and power wire brush to remove all loose rust, millscale, etc., to ISO 8501-1, ST3. Degrease with Dacrylate Thinner R5. Apply one coat of Vinaprime 41 HB Anti-Corrosion Primer to a dry film thickness of 50 microns.
Galvanising (new): Ensure surface is cleaned and dry. Pre-treat with Dacrylate Mordant Solution ('T' Wash) (Ref.: 150-23).
Galvanising (weathered): Use stiff brush to remove any deposits of white zinc salts. Degrease with Dacrylate Thinner R5.
Application Conditions: Temperature minimum 5°C
Humidity less than 90% RH
Application Methods: Brush: Apply using a 'full' wet brush. Avoid excessive 'brushing out'. Do not 'lay-off'. A wet film thickness of 190 microns will give a dry film thickness of 75 microns.
Roller: As for brush application, taking care to apply specified wet film thickness.
Spray: Vinadac HB can be applied using conventional, airless and HVLP spray methods. 5-10% of Dacrylate Thinner R5 may be required to give optimum spray characteristics.
Brush or roller is the preferred method for use on damp surfaces.
Clean-up: Dacrylate Thinner R1 or R70.
Health and Safety: For more information request relevant Material Safety Datasheet.

The above information is general information on the product but without warranty. Since conditions of service and application are beyond our control we cannot accept claims for loss, damage etc., based on this information. Dacrylate will not accept any claim for consequential or incidental damages.