Vinadac High Solids Sheen Finish
(Airless Spray Grade)

Vinadac High Solids Sheen Finish
(Airless Spray Grade)

Reference No.: 45-Line

A modified vinyl with rust-inhibitive pigment.

Fully compliant with Environment Protection Act (1990) as required by Guidance Note PG6/23 (97).

Typically used as a high solids, high build coating for the protection of steel and galvanised steel in aggressive environments.

Colours available: To customer order, contact us for more information
Appearance Of Dried Film: Sheen finish
Volume Solids: 53%
Dry Film Thickness: Typical 75 microns / Range 50-100 microns
Theoretical Coverage: 7.0m² per litre at 75 microns
Drying Time At 20°C: Touch Dry: 2 hours
Film Dry: 4-5 hours
Overcoat: 4-5 hours
(will vary with temperature, air movements, etc.)
V.O.C.: 410 grm/litre (may vary with colour)
Packaging: 5 litre and 20 litre open-top containers
Shelf Life: 2 years or longer in unopened containers when stored under cover in good storage conditions.
Storage: Under cover with temperature range of 5°C to 32°C.
Due to the protective nature of the product, some chalking may occur on exposure/weathering. This is purely aesthetic and will not detract from the performance, durability and longevity of the system. It should therefore be borne in mind that this phenomenon may be more visible on certain bright/bold colours.
Surface Preparation: Mild steel, clean and free of millscale: Thoroughly degrease with Dacrylate Thinner R5. Apply one coat of Vinaprime 41 HB Anti-Corrosion Primer Ref.: 41-120, to a dry film thickness of 50 microns.
Mild steel, corroded and/or millscale present: Abrasive blasting to ISO 8501-1 SA2.5 is the preferred method.
Manual clean: Chip scrape and power wire-brush to remove all loose rust, milscale, etc., to ISO 8501-1 ST3. Degrease with Dacrylate Thinner R5. Apply one coat of Vinaprime 41 HB Anti-Corrosion Primer Ref.: 41-120, to a dry film thickness of 50 microns.
Galvanising (new): Ensure surface is clean and dry. Pre-treat with Dacrylate Mordant Solution ('T' Wash) Ref.: 150-23.
Galvanising (weathered): Use stiff brush to remove any deposits of white zinc salts. Wash down with detergent water to remove salts, etc., rinse and dry off.
Application: Airless spray:
Minimum Tip Pressure: 2500psi (160 Bar)
Tip Size: 15-17 Thou (0.38m/m to 0.43m/m)
Apply to an approximate wet film thickness of 140 microns to achieve a dry film thickness of 75 microns.
N.B.: Brush application limited to small areas. Certain products retain solvents for longer periods, which will affect plasticizers within the plastic packaging causing damage to the finish. It is therefore not recommended that finished painted products be wrapped in bubble wrap, plastic sleeves, etc., until coatings are fully cured as this can cause damage to the finish especially when stacked or stored in sunlight/elevated tempertures.
Damage can also occur from condensation caused by fluctuations in temperature consequently causing a 'greenhouse' effect within the packaging.
Clean-up: Dacrylate Thinner R5
Health and Safety: For more information request relevant Material Safety Datasheet.

The above information is general information on the product but without warranty. Since conditions of service and application are beyond our control we cannot accept claims for loss, damage etc., based on this information. Dacrylate will not accept any claim for consequential or incidental damages.