Products
Epidac 112
Ref Number: 90-200
Category: Epidac
Dacrylate Epidac 112 is a high-solids epoxy coating that provides long-term protection of steel and galvanised fabrications.
Specifications
| Features and benefits: |  • BBA approved for Highways England Item 112 • High volume solids • Low VOC content – compliant with EPA PG23/6 • Offers enhanced barrier protection using laminar MIO pigmentation • Excellent adhesion to galvanised steelwork |
| Coating type: | High solids epoxy with 80% MIO pigmentation (with low temperature curing properties) |
| Appearance: | Low sheen finish |
| Colours available: | Grey (approximately BS 4800 00-A-09) |
| Theoretical coverage: | 5m² per litre at 150 microns dry film thickness |
| Sag tolerance: | 300 microns wet film thickness |
| Film thickness: | Wet film thickness: Typical 200 microns / Range 130-235 microns Dry film thickness: Typical 150 microns / Range 100-175 microns |
| VOC: | 213grm/ltr EPA Method 24 102grm/kg calculated from formulation to satisfy EU Solvent Emissions Directive |
| % Volume solids: | 75% calculated from laboratory formulation |
| Drying time | 5°C: 8hrs touch dry, 16hrs firm dry, Overcoat after 10hrs* 10°C: 4hrs touch dry, 8hrs firm dry, Overcoat after 2hrs* 20°C: 6hrs touch dry, 4hrs firm dry, Overcoat after 4hrs* 30°C: ---** touch dry, 2hrs firm dry, Overcoat after 2hrs* *With epoxy or polyurethane **Value not determined Drying time will vary with temperature, air movement, etc. Overcoating should either be done with the product itself, epoxy-ester, pitch-epoxy, or oleo-resinous paints. Maximum overcoating is 5 days at 20°C. After this period, the surface should be lightly abraded and ‘solvent wiped prior to applying further coats. |
| Mixing ratio: | 4-parts base to 1-part activator |
| Pack size: | 5L |